酯化固体酸颗粒催化剂的研制及应用(任务书,开题报告,论文8000字)
摘 要
本文采用浸渍法制备SO42-/SnO2/Al2O3固体酸催化剂，并对催化剂的制备条件进行优化。研究三羟甲基丙烷和油酸的酯化反应，得到催化剂最佳制备条件：硫酸浓度为3 mol/L，浸泡时间为3 h，碳酸钙添加量为30%，焙烧温度为500℃，焙烧时间为5 h，制得的催化剂活性最强，此时三羟甲基丙烷和油酸的酯化率为89%。碳酸钙添加量为30%时，催化剂的比表面积最大，平均孔径最大，活性最强。
关键词 固体酸催化剂 酯化反应 制备条件
Preparation and application of esterification
solid acid particle catalyst
Abstract
Tinhydroxide, aluminium oxide, red clay, polyetheiene glycol, sesbania powder, calciun carbonate was the raw material for this article. The catalyst was prepared by impregnation method and was used for esterification of trimethylol propane and oleic acid. The optimum preparation conditions was investigated, Sulfuric acid concentration is 3 mol/L, the soaking time is 3 h, the roasting time is 5 h, the roasting temperature is 550 ℃. In the reaction of controlling the amount of calcium carbonate. The specific surface area and average pore diameter of different calcium carbonate content were determined. The catalyst under optimum preparation conditions was found. [资料来源：http://doc163.com]
KEYWORDS: Solid acid catalyst; Esterification reaction; Preparation condition
目 录
摘 要 I
Abstract II
第一章 文献综述 1
1.1 前言 1
1.2 固体酸催化剂的应用
1.2.1酯化反应 1
1.2.2加氢裂解反应 2
1.2.3脱水反应 2
1.2.4聚合缩合反应 2
1.2.5异构化反应.......... 2
1.3 固体酸催化剂的分类及在酯化反应中的研究近况 2
1.3.1 固载化液体酸 3
1.3.2 负载型简单氧化物固体酸 3
1.3.3 金属盐 3
1.3.4 杂多酸 3
1.3.5固体酸超强酸 4
1.4 本课题的研究目的与意义 5 [资料来源：https://www.doc163.com]
第二章 实验部分 5
2.1 实验试剂与仪器 5
2.1.1 实验试剂 5
2.1.2 实验仪器 5
2.2 实验方法 6
2.2.1催化剂的制备 6
2.2.2 催化剂的表征 7
2.2.3 反应性能测试 7
2.2.4 产物分析及方法 8
第三章 结果与讨论 8
3.1致孔剂添加量对催化剂活性的影响 8
3.1.1 反应性能表征 9
3.1.2 BET表征..........10
3.2浸渍时间对催化活性的影响 13
3.3浸渍浓度对催化活性的影响 14
3.4焙烧时间对催化活性的影响 15
3.5焙烧温度对催化活性的影响 15
第四章 结论与展望 16
4.1 结 论 16
4.2 展 望 16
参考文献 17
致 谢 19 [资料来源：www.doc163.com]